common fiber cement board
lonrace
class A
yes
black, grey
4.5-18mm
1.2-1.4g/cm3
CE ISO9001
Cellulose Fiber, pulp
Exterior Wall Panel; Partition wall
| TEST ITEM | UNIT | TEST RESULT | |
| Bending Strength | Mpa | 6MM | Width: >18 |
| | | | Length: >14 |
| | | 9MM & 12MM-18MM | Width: >16 |
| | | | Length: >13 |
| Water Absorption | % | <10% | |
| Thermal Contraction | % | <0.06(w/mk) (30 °C ) | |
| Density | g/cm3 | 1.3-1.4 | |
| Freezing Resistance | After 25 Freezing cycles | No Delaminated | |
| Combustibility | - | Incombustible (class A) | |
| Fire Resistance Limit | Min | 2 Layers Mineral Wool:180 | |
| Thermal Conductivity | W/(m • k) | <0.12 | |
| Wall Average Acoustical Deduction Factor | dB | 2 Layers 50mm Mineral Wool: 44 | |
| Impact Strength | kg/C | :2.0 | |
| Watertight | 24h | No Water Drop at the bottom for 24/h | |
| TEST ITEM | UNIT | TEST RESULT | |
| Bending Strength | Mpa | 6MM | Width: >18 |
| | | | Length: >14 |
| | | 9MM & 12MM-18MM | Width: >16 |
| | | | Length: >13 |
| Water Absorption | % | <10% | |
| Thermal Contraction | % | <0.06(w/mk) (30 °C ) | |
| Density | g/cm3 | 1.3-1.4 | |
| Freezing Resistance | After 25 Freezing cycles | No Delaminated | |
| Combustibility | - | Incombustible (class A) | |
| Fire Resistance Limit | Min | 2 Layers Mineral Wool:180 | |
| Thermal Conductivity | W/(m • k) | <0.12 | |
| Wall Average Acoustical Deduction Factor | dB | 2 Layers 50mm Mineral Wool: 44 | |
| Impact Strength | kg/C | :2.0 | |
| Watertight | 24h | No Water Drop at the bottom for 24/h | |